Lam.CoS
Some say that all good steel already are
developed - we are not sure about that.
Till now, we haven’t disclosed much information
about our new laminated Cobalt Special steel
but what we can say is - this is a new, very good
steel! The alloy mix is C 1.1%. Cr. 16%. W
0.3%. Mo 1.5%. V 0.3%. Co 2.5%. As with our
other steel, this steel will be used as a centre
steel, with 420J2 layers, and we usually bring a
hardness of around HRC 60 to the centre steel.
We have tested the CoS steel at the CATRA
test laboratories in UK and found very good
qualities.
A reflection we made when testing the cobalt
steel is that this steel gets scary sharp. We
have actually never seen a steel which gets so
incredibly sharp. And, our field tests show upon
a very good edge retention and no signs of
edge break. The only negative matter is that it is
around 50-60% more expensive than the VG10
steel. Our experience of this new Cobalt Special
steel is so good that we believe that quite many
new knife models will have this steel. Still, we
won’t reject the 3G or VG10 steels, they have
proven to be extremely reliable.
Никто не будет с нуля формировать полноразмерные плашки для лимиты в 750 штук. Обычная механика Грипа, одетая в Ж10 (без внутренних полостей, зачем лишние операции при фрезеровке)
митяй писал(а):Никто не будет с нуля формировать полноразмерные плашки для лимиты в 750 штук. Обычная механика Грипа, одетая в Ж10 (без внутренних полостей, зачем лишние операции при фрезеровке)
+1
Винтик в середине рукояти кагбэ намекаэ
Не стоит прогибаться под изменчивый Мир,
Пусть, лучше, он прогнется под нас!
Симпатичный ножик в винтажном стиле
Что-то я пресытился современными дизайнами, вот всё чаще хочется иметь на кармане вот такой незатейливый ножичек.
Да и нож такой в глазах обывателя выглядит более мирно чем Грипы, Блюры, Крысы, 710-е, Мили, Зины и прочие тактические закосы.