http://faq.customtacticals.com/steels/s ... s_n690.phpN690 сталь производит Bohler Uddeholm.
It's made by Bohler Edelstahl in Austria. It is a 440C base alloy with additional Molybdenum and Cobalt. These additions allow for slighty better corrosion resistance than 440C (N685), high temperature tempering (bearing applications), and roughly 2 points higher attainable hardness than 440C. The slightly higher corrosion resistance and higher attainable hardness is why the world wide market likes this alloy for specialty cutting tools and cutlery over generic 440C. Bohler markets this alloy throughout the world but not currently in the US. This is why it is seen on a lot of knives produced overseas and not those produced domestically.
По составу эта сталь приблизительно соответствует 440C, но содержит больше молибдена и кобальта. Иногда ее называют австрийской 440C или австрийской кобальтовой нержавейкой.
____________440C___________N690
C%_______0.95 - 1.20________1.05
Cr________16.00-18.00_______17
Mo__________0.75___________1.1
V____________-____________0.1
Co___________-____________1.5
Отличается очень высокой коррозионной стойкостью и возможностью закалить ее до 60 HRC.
Считается хорошей сталью для outdoor длинномеров и тактических ножей, которым необходимо иметь не только стойкую кромку, но и способность выдерживать ударные и боковые нагрузки (на поворот и на излом).
Из этой стали делают ножи многие европейские филиалы, включая Boker и Spyderco. Также некоторые модели Benchmade и почти все Extrema Ratio.
In the latest issue of "Tactical Knives", Jerry Hossom is quoted (in the artical on the upcoming Spyderco/Hossom fixed blades collaboration) as having said that "N690 behaves a lot like BG-42." Jerry knows his stuff, so it must be pretty decent steel.
I really like the performance of N690 in my Monochrome (59HRC in mine). To me, it seems to take a finer edge than 440C, which is what you would expect with a trace of Vanadium to refine the grain structure. When I did side by side edge retention testing on manila rope, I found edge retention of N690 to be on the order of VG10, 154CM et. al. Really lovely stuff.
Кто что думает про эту стальку?
Не популярна скажете? ))
, у меня Монохром, после длительного ношения периодически покрывается питтингом, все это дело конечно стирается резинкой без проблем и смазывается баллистолом, но требует эта сталька должного ухода 