Твёрдость стали на ножах Spyderco
Искал данные о твердости стали на PM2 S110V и попалась мне тема на Spyderco forum по твердости сталей на ножах Spyderco, решил тиснуть её здесь
https://forum.spyderco.com/viewtopic.php?f=2&t=83847
сталь,модель, твердость HRC:
MAXAMET Manix 2 LW - (66.2 - 69) HRC
MAXAMET Paramilitary 2 - 68 HRC
H-1 (SE at the edge, not sure which model) - 68 HRC
MAXAMET Mule - (67 - 68) HRC
REX45 Military - (66.3 - 67) HRC
REX45 Paramilitary 2 - (65 - 66.7) HRC
ZDP-189 Mule - 66.4 HRC
K390 Police 4 G-10 - (64 -65.5) HRC
4V Manix 2 (Marbled CF) - 65 HRC
4V Para 3 (St. Nicks Exclusive) - (64.8 -65) HRC
H-1 (PE at the edge, not sure which model) - (64-65) HRC
ZDP-189 Endura 4 - (63 -65) HRC
REX45 Para 3 - 64.7 HRC
M4 Paramilitary 2 - 64.3 HRC
M4 Manix 2 - 64.2 HRC
M4 Shaman - (63.9 - 64) HRC
ZDP-189 Delica 4 (Saber) - (63.5 - 64) HRC
S110V Military - (63-64) HRC
K390 Mule - (62-64) HRC
Cruwear Manix 2 - (63.2 - 63.7) HRC
M4 Gayle-Bradley 2 - 63.2 HRC
ZDP-189 Dragonfly 2 - 63.1 HRC
52100 Mule - 63.1 HRC
10V K2 - 63 HRC
M4 Para 3 - 63 HRC
B75P Mule - (62-63) HRC
Cruwear Military - 62.9 HRC
52100 Paramilitary 2 - 62.8 HRC
Cruwear Mule (re-release) - (62.1 -62.8) HRC
Cruwear Paramilitary 2 - (62 - 62.8) HRC
Super Blue Mule - 62.5 HRC
PMA11 Mule - 62.5 HRC
M4 Mule - (60.8 - 62.5 HRC)
M4 Gayle-Bradley 1 - 62.5 HRC
K390 Urban - 62.5 HRC
M390 Paramilitary 2 - 62 HRC
S110V Manix 2 - 62 HRC
XHP Chaparral FRN - 62 HRC
Cruwear Paramilitary 2 - 62 HRC
S110V Paramilitary 2 - (60.9 - 62) HRC
PSF27 Mule - 61.9 HRC
Cruwear Para 3 - 61.7 HRC
XHP Para 3 - 61.5 HRC
Cruwear Military - 61.1 HRC
M390 Military - 61 HRC
Super Blue Calypso Jr. - (60.8 - 61) HRC
S30V Amalgam - 60.7 HRC
20CV Manix 2 - 60.6 HRC
M390 Mule - (59.2 - 60.5) HRC
XHP Military - 60.5 HRC
S30V Para 3 - 60.3 HRC
XHP Mule - (60 - 60.3) HRC
S30V Manix 2 - 60.1 HRC
BD1N Para 3 LW - 60 HRC
BD1N UKPK - 60 HRC
S110V Mule - 60 HRC
S90V Military - 60 HRC
S30V Manix 2 (Backlock) - 60 HRC
S30V Military - 60 HRC
S35VN Native 5 LW - 60 HRC
RWL34 Mule - 60 HRC
20CV Mule - 60 HRC
M390 Para 3 - (59.6 -60) HRC
S90V Manix 2 LW - 59.9 HRC
S35VN Para 3 - (59- 59.6) HRC
S90V Mule - 59.2 HRC
BD1 UKPK SLIPIT - 59.1 HRC
S30V Paramilitary 2 - (58.8 - 59) HRC
S30V Delica Wharncliffe - 59 HRC
S30V Delica - 59 HRC
BD1 Manix 2 LW - 59 HRC
ELMAX Mule - (58.3 -58.5) HRC
LC200N Spydiechef - (57.8 - 58.1) HRC
VG-10 Delica 4 - 58 HRC
VG-10 Endura - 57.9 HRC
N690 Roadie - 57.8
8Cr13MoV Tenacious - 57.6 HRC
8Cr13MoV Tenacious (Red) - 56.8 HRC
LC200N Mule - 56.8 HRC
"Keep in mind these are approximate numbers not exact numbers. Corrections and additions are always welcome
"Edit*
I feel like I should expand on this point a little and remind anyone reading this list of a few things.
1st- these numbers are usually from a single source, who ran a single test, on a single knife.... needless to say, the results are NOT scientific. And as such they are not necessarily accurate. This is why corrections and additional information is always welcome. The more data points, the more accurate the information. PLEASE take these numbers with a grain of salt.
2nd- There is way more to a good knife than an HRC number.
You can have two knives with the same steel and same HRC number, and different heat treat protocols, and those knives will perform differently from eachother.
It bears repeating, the HRC number is ONE factor out of MANY, you can not judge a knife on it's HRC alone. A high or a low HRC does not tell the whole story, it's just a piece of the puzzle."
https://forum.spyderco.com/viewtopic.php?f=2&t=83847
сталь,модель, твердость HRC:
MAXAMET Manix 2 LW - (66.2 - 69) HRC
MAXAMET Paramilitary 2 - 68 HRC
H-1 (SE at the edge, not sure which model) - 68 HRC
MAXAMET Mule - (67 - 68) HRC
REX45 Military - (66.3 - 67) HRC
REX45 Paramilitary 2 - (65 - 66.7) HRC
ZDP-189 Mule - 66.4 HRC
K390 Police 4 G-10 - (64 -65.5) HRC
4V Manix 2 (Marbled CF) - 65 HRC
4V Para 3 (St. Nicks Exclusive) - (64.8 -65) HRC
H-1 (PE at the edge, not sure which model) - (64-65) HRC
ZDP-189 Endura 4 - (63 -65) HRC
REX45 Para 3 - 64.7 HRC
M4 Paramilitary 2 - 64.3 HRC
M4 Manix 2 - 64.2 HRC
M4 Shaman - (63.9 - 64) HRC
ZDP-189 Delica 4 (Saber) - (63.5 - 64) HRC
S110V Military - (63-64) HRC
K390 Mule - (62-64) HRC
Cruwear Manix 2 - (63.2 - 63.7) HRC
M4 Gayle-Bradley 2 - 63.2 HRC
ZDP-189 Dragonfly 2 - 63.1 HRC
52100 Mule - 63.1 HRC
10V K2 - 63 HRC
M4 Para 3 - 63 HRC
B75P Mule - (62-63) HRC
Cruwear Military - 62.9 HRC
52100 Paramilitary 2 - 62.8 HRC
Cruwear Mule (re-release) - (62.1 -62.8) HRC
Cruwear Paramilitary 2 - (62 - 62.8) HRC
Super Blue Mule - 62.5 HRC
PMA11 Mule - 62.5 HRC
M4 Mule - (60.8 - 62.5 HRC)
M4 Gayle-Bradley 1 - 62.5 HRC
K390 Urban - 62.5 HRC
M390 Paramilitary 2 - 62 HRC
S110V Manix 2 - 62 HRC
XHP Chaparral FRN - 62 HRC
Cruwear Paramilitary 2 - 62 HRC
S110V Paramilitary 2 - (60.9 - 62) HRC
PSF27 Mule - 61.9 HRC
Cruwear Para 3 - 61.7 HRC
XHP Para 3 - 61.5 HRC
Cruwear Military - 61.1 HRC
M390 Military - 61 HRC
Super Blue Calypso Jr. - (60.8 - 61) HRC
S30V Amalgam - 60.7 HRC
20CV Manix 2 - 60.6 HRC
M390 Mule - (59.2 - 60.5) HRC
XHP Military - 60.5 HRC
S30V Para 3 - 60.3 HRC
XHP Mule - (60 - 60.3) HRC
S30V Manix 2 - 60.1 HRC
BD1N Para 3 LW - 60 HRC
BD1N UKPK - 60 HRC
S110V Mule - 60 HRC
S90V Military - 60 HRC
S30V Manix 2 (Backlock) - 60 HRC
S30V Military - 60 HRC
S35VN Native 5 LW - 60 HRC
RWL34 Mule - 60 HRC
20CV Mule - 60 HRC
M390 Para 3 - (59.6 -60) HRC
S90V Manix 2 LW - 59.9 HRC
S35VN Para 3 - (59- 59.6) HRC
S90V Mule - 59.2 HRC
BD1 UKPK SLIPIT - 59.1 HRC
S30V Paramilitary 2 - (58.8 - 59) HRC
S30V Delica Wharncliffe - 59 HRC
S30V Delica - 59 HRC
BD1 Manix 2 LW - 59 HRC
ELMAX Mule - (58.3 -58.5) HRC
LC200N Spydiechef - (57.8 - 58.1) HRC
VG-10 Delica 4 - 58 HRC
VG-10 Endura - 57.9 HRC
N690 Roadie - 57.8
8Cr13MoV Tenacious - 57.6 HRC
8Cr13MoV Tenacious (Red) - 56.8 HRC
LC200N Mule - 56.8 HRC
"Keep in mind these are approximate numbers not exact numbers. Corrections and additions are always welcome
"Edit*
I feel like I should expand on this point a little and remind anyone reading this list of a few things.
1st- these numbers are usually from a single source, who ran a single test, on a single knife.... needless to say, the results are NOT scientific. And as such they are not necessarily accurate. This is why corrections and additional information is always welcome. The more data points, the more accurate the information. PLEASE take these numbers with a grain of salt.
2nd- There is way more to a good knife than an HRC number.
You can have two knives with the same steel and same HRC number, and different heat treat protocols, and those knives will perform differently from eachother.
It bears repeating, the HRC number is ONE factor out of MANY, you can not judge a knife on it's HRC alone. A high or a low HRC does not tell the whole story, it's just a piece of the puzzle."
Последний раз редактировалось GeorgCH 22 сен 2020, 18:27, всего редактировалось 1 раз.
Life is a series of choices.
- GeorgCH
- Гуру-найфоман
- Сообщения: 13526
- Зарегистрирован: 01 окт 2009, 11:47
- Откуда: Киев
- Благодарил (а): 5730 раз
- Поблагодарили: 9587 раз
Твёрдость стали на ножах Spyderco
вот тоже тема интересная для любителей тонкого сведения
Behind the Edge
https://forum.spyderco.com/viewtopic.php?f=2&t=73097
Behind the Edge
https://forum.spyderco.com/viewtopic.php?f=2&t=73097
Life is a series of choices.
- rw-odessa
- Найфоман
- Сообщения: 850
- Зарегистрирован: 03 мар 2009, 11:48
- Откуда: Odessa
- Благодарил (а): 9 раз
- Поблагодарили: 9 раз
- Контактная информация:
Твёрдость стали на ножах Spyderco
H1 пишут 68, это не та сталь, что на Salt серии, может ошибка 58?
"Чего же ты пугаешься? С человеком происходит то же, что и с деревом.
Чем настойчивее стремится он вверх, к свету, тем с большей силой устремляются корни его в глубь земли, вниз, во мрак – во зло."
Чем настойчивее стремится он вверх, к свету, тем с большей силой устремляются корни его в глубь земли, вниз, во мрак – во зло."
- seaman
- Найфоман-эксперт
- Сообщения: 2856
- Зарегистрирован: 30 окт 2009, 11:29
- Откуда: Київ
- Благодарил (а): 705 раз
- Поблагодарили: 1190 раз
- Контактная информация:
Твёрдость стали на ножах Spyderco
Теж Н1 здивувала. Але ж пишуть, що дані відкриті, де, хто, чим наміряв....
...У світі хижаків, завжди винна жертва...
- GeorgCH
- Гуру-найфоман
- Сообщения: 13526
- Зарегистрирован: 01 окт 2009, 11:47
- Откуда: Киев
- Благодарил (а): 5730 раз
- Поблагодарили: 9587 раз
Твёрдость стали на ножах Spyderco
Sal Glesser said: ↑
"When the foundry rolls the H1, they roll to two different hardness, we end up with 58 for the blade material and considerably lower spec for the lock material. Not meaning to be disrespectful, but the two hardnesses are controlled by the rolling process.
Dick Barber, metallurgist for Crucible steels was curious as to why the H1 steel was testing so well and wanted to do metallurgical testing on the material. We sent them samples and they did their tests. In their micro hardness testing, they found the H1 was differentially hardening. Their explanation was as I described.
The were getting over 60 (64/65 as I remembber the report) at the edge of the blade, 58 at the spine and various hardness in between as they went from the spine to the edge.
The serrted edge version was higher (68 as I remember) which Mr. Barber attributed to the extra "work" (heat) required to serrate the edge over just sharpening as on the plain edge.
If you would like I can fax you, or mail you a copy of the report. Email me your address."
https://www.bladeforums.com/threads/h1- ... ost4484958
"When the foundry rolls the H1, they roll to two different hardness, we end up with 58 for the blade material and considerably lower spec for the lock material. Not meaning to be disrespectful, but the two hardnesses are controlled by the rolling process.
Dick Barber, metallurgist for Crucible steels was curious as to why the H1 steel was testing so well and wanted to do metallurgical testing on the material. We sent them samples and they did their tests. In their micro hardness testing, they found the H1 was differentially hardening. Their explanation was as I described.
The were getting over 60 (64/65 as I remembber the report) at the edge of the blade, 58 at the spine and various hardness in between as they went from the spine to the edge.
The serrted edge version was higher (68 as I remember) which Mr. Barber attributed to the extra "work" (heat) required to serrate the edge over just sharpening as on the plain edge.
If you would like I can fax you, or mail you a copy of the report. Email me your address."
https://www.bladeforums.com/threads/h1- ... ost4484958
Life is a series of choices.
- Gott
- Найфоман-эксперт
- Сообщения: 2443
- Зарегистрирован: 20 май 2008, 00:27
- Откуда: Kiev
- Благодарил (а): 146 раз
- Поблагодарили: 92 раза
Твёрдость стали на ножах Spyderco
Скорей 48.
Ну вот. А про твёрдость HAP40 в ламинате, не написали. Как и про твёрдость ZDP-189, в пакете, на Kaly 3,5.
- pr13s7
- Найфоман-эксперт
- Сообщения: 2138
- Зарегистрирован: 18 янв 2013, 10:12
- Откуда: Киев
- Благодарил (а): 58 раз
- Поблагодарили: 56 раз
Твёрдость стали на ножах Spyderco
то что Н1 калят на более чем 60 давно известный факт. это делается чтобы хоть как-то компенсировать то, что сталь специфическая и агресивного реза (да и вообще реза) там нет. так что это не опечатка
твердость ламината померять прямо скажем нетривиально. т.к. для замера нужны две паралельные плоскости на куске замеряемой стали, а сама НАР40 или ZDP выходят из обкладок какраз в местах которые сложно назвать параллельными
твердость ламината померять прямо скажем нетривиально. т.к. для замера нужны две паралельные плоскости на куске замеряемой стали, а сама НАР40 или ZDP выходят из обкладок какраз в местах которые сложно назвать параллельными
- GeorgCH
- Гуру-найфоман
- Сообщения: 13526
- Зарегистрирован: 01 окт 2009, 11:47
- Откуда: Киев
- Благодарил (а): 5730 раз
- Поблагодарили: 9587 раз
- GeorgCH
- Гуру-найфоман
- Сообщения: 13526
- Зарегистрирован: 01 окт 2009, 11:47
- Откуда: Киев
- Благодарил (а): 5730 раз
- Поблагодарили: 9587 раз
- GeorgCH
- Гуру-найфоман
- Сообщения: 13526
- Зарегистрирован: 01 окт 2009, 11:47
- Откуда: Киев
- Благодарил (а): 5730 раз
- Поблагодарили: 9587 раз
- GeorgCH
- Гуру-найфоман
- Сообщения: 13526
- Зарегистрирован: 01 окт 2009, 11:47
- Откуда: Киев
- Благодарил (а): 5730 раз
- Поблагодарили: 9587 раз
Твёрдость стали на ножах Spyderco
Проверка удержания кромки 48 ножевых сталей
https://knifesteelnerds.com/2020/05/01/ ... fe-steels/
https://forum.spyderco.com/viewtopic.php?f=2&t=86503
https://knifesteelnerds.com/2020/05/01/ ... fe-steels/
https://forum.spyderco.com/viewtopic.php?f=2&t=86503
Life is a series of choices.
- GeorgCH
- Гуру-найфоман
- Сообщения: 13526
- Зарегистрирован: 01 окт 2009, 11:47
- Откуда: Киев
- Благодарил (а): 5730 раз
- Поблагодарили: 9587 раз
Твёрдость стали на ножах Spyderco
Для кого предназначена книга?
В книге рассматриваются основные параметры, которые влияют на производительность ножа, такие как геометрия кромки, выбор стали и термообработка. Это описывается с помощью различных механизмов, влияющих на ножи, включая: изгиб и изгиб, скалывание и разрушение, коррозию, сохранение кромки, шлифуемость и полируемость и т. Д. Представлены различные марки ножевых сталей, включая их состав, микроструктуру, ударную вязкость, удержание кромки, твердость. , и коррозионная стойкость. Процесс термической обработки и обработки стали подробно описан, включая то, что происходит на каждом этапе, например, аустенизация, закалка, отпуск, криообработка и многое другое. Это включает в себя объяснение изменений микроструктуры, целей каждого этапа и способов оптимизации различных этапов термообработки. И я дал рекомендации по специальной термообработке для большинства основных сталей для ножей. Это все, о чем производители ножей должны заботиться при создании высокопроизводительных ножей. А энтузиасты ножей могут узнать, какие аспекты учитывают производители ножей, на что обращать внимание на свои ножи и как настроить свои процедуры заточки с точки зрения угла кромки и обработки для различных целей.
Life is a series of choices.
- GeorgCH
- Гуру-найфоман
- Сообщения: 13526
- Зарегистрирован: 01 окт 2009, 11:47
- Откуда: Киев
- Благодарил (а): 5730 раз
- Поблагодарили: 9587 раз
Твёрдость стали на ножах Spyderco
тесты XHP,"torture"
https://www.instagram.com/p/CMvOHLpDFu5/
https://www.instagram.com/p/CMvOHLpDFu5/
Life is a series of choices.
- Artvitel
- Начинающий найфоман
- Сообщения: 148
- Зарегистрирован: 10 ноя 2018, 16:03
- Откуда: Odessa
- Благодарил (а): 68 раз
- Поблагодарили: 31 раз
Твёрдость стали на ножах Spyderco
На Spyderco Forum есть отдельная тема по твердости на ножах Mule Team
https://forum.spyderco.com/viewtopic.ph ... 9c4032b4f7
Там уже и по МТ28, со сталью SPY27 замеры есть: 61.5 +/- 0.5 HRC
https://forum.spyderco.com/viewtopic.ph ... 9c4032b4f7
Там уже и по МТ28, со сталью SPY27 замеры есть: 61.5 +/- 0.5 HRC
У вас нет необходимых прав для просмотра вложений в этом сообщении.
«Инженерная мысль Человечества, прежде всего, воплощается в Оружии» Леонардо Да Винчи
- Феникс
- Найфоман-эксперт
- Сообщения: 2159
- Зарегистрирован: 19 ноя 2014, 19:13
- Откуда: Черкассы
- Благодарил (а): 277 раз
- Поблагодарили: 241 раз
Твёрдость стали на ножах Spyderco
А вот hap 40 ничего нет, кто будет видеть информацию, о этой стали, поделитесь
- GeorgCH
- Гуру-найфоман
- Сообщения: 13526
- Зарегистрирован: 01 окт 2009, 11:47
- Откуда: Киев
- Благодарил (а): 5730 раз
- Поблагодарили: 9587 раз
Твёрдость стали на ножах Spyderco
Если кому-то еще интересно, влияет ли покрытие DLC на тестирование HRC
Текстовая ссылка на видео - https://youtu.be/lpbI8ggRjyw
Текстовая ссылка на видео - https://youtu.be/lpbI8ggRjyw
Life is a series of choices.
- totorro
- Найфоман
- Сообщения: 1229
- Зарегистрирован: 25 июл 2012, 12:31
- Откуда: Обухов
- Благодарил (а): 25 раз
- Поблагодарили: 52 раза
Твёрдость стали на ножах Spyderco
Всем привет
Вопрос не совсем про твердость но про стали. Какие стали на спаях патинируют (не ржавеют)? Хочется чего то необычного)
Вопрос не совсем про твердость но про стали. Какие стали на спаях патинируют (не ржавеют)? Хочется чего то необычного)
- dragonfly635
- Найфоман
- Сообщения: 1271
- Зарегистрирован: 26 сен 2011, 15:34
- Откуда: Бандерштадт
- Благодарил (а): 626 раз
- Поблагодарили: 696 раз
- Контактная информация:
Твёрдость стали на ножах Spyderco
totorro, HAP40, K390, Rex45 точно, по другим не скажу, это с собственного опыта
- GeorgCH
- Гуру-найфоман
- Сообщения: 13526
- Зарегистрирован: 01 окт 2009, 11:47
- Откуда: Киев
- Благодарил (а): 5730 раз
- Поблагодарили: 9587 раз
Твёрдость стали на ножах Spyderco
после такого теста я к390 от спайдерко зауважал
Текстовая ссылка на видео - https://youtu.be/E-c3LxQbcqg
Текстовая ссылка на видео - https://youtu.be/E-c3LxQbcqg
Life is a series of choices.
- Maxkon
- Найфоман-эксперт
- Сообщения: 3889
- Зарегистрирован: 26 июл 2010, 12:31
- Откуда: Київ
- Благодарил (а): 275 раз
- Поблагодарили: 383 раза
- Контактная информация:
Твёрдость стали на ножах Spyderco
Ну да 390 на полисе это очень и очень. А вот VG10 на новых полисах с FRN полное .... - пластилин. Садится "мгновенно", загибается кромка. Такое впечатление: забыли закалить.
P.S. Хотя, может быть, это мне так повезло, но не двух же ножах...
P.S.S. зачем так издеваться над ножом.
- Феникс
- Найфоман-эксперт
- Сообщения: 2159
- Зарегистрирован: 19 ноя 2014, 19:13
- Откуда: Черкассы
- Благодарил (а): 277 раз
- Поблагодарили: 241 раз
Твёрдость стали на ножах Spyderco
А Maxamet кто нибудь юзал продолжительное время?
Согласно схемы в первом посте, эта сталь имеет выше всех показатели, но и возможно так же ловит выкрашивания рк?
Согласно схемы в первом посте, эта сталь имеет выше всех показатели, но и возможно так же ловит выкрашивания рк?
-
- Новичок
- Сообщения: 9
- Зарегистрирован: 20 окт 2021, 14:32
- Откуда: Kyiv
- Благодарил (а): 7 раз
- Поблагодарили: 15 раз
Твёрдость стали на ножах Spyderco
Купил пару месяцев назад ПМ2 с Максаметом, очень приятный цвет клинка, естественный стоунвош такой, ухаживал(балистол и насухо, через день), рез космический даже на заводской заточке.
Но… уронил на ковёр(!) он воткнулся и под весом рукоятки упал на бок и потерял кончик. Сломался такое чувство, не от удара, а процессе падения на бок уже внизу после того как воткнулся в ковёр. Так мне показалось. Очень неприятно, сломался как будто керамический… опыта с такими твёрдыми порошками до этого я не имел. Теперь имею) отдал мастеру на ремонт, посмотрим.
Последний раз редактировалось ДионКассий 20 окт 2021, 16:54, всего редактировалось 1 раз.